UPVC ROOFING SHEET, TEJAS DE UPVC
T1130 White UPVC roofing sheets, PVC plastic roof sheet is one of the most popular styles all over the world. The width is 1130 mm, the length could be customized. It is suitable for most buildings, it can save the cost of cooling and makes the building tidy and lofty.
Blanca tejas de UPVC con cresta baja, el 1130mm anchos eco roof teja termoacustica UPVC esta muy popular en Latina America para techos, cubiertas, drywall, etc
T1130 thermal insulation UPVC roofing sheets:
| Descreption |
Picture of structure |
| Width |
1130mm |
 |
| Effective width |
1050mm |
| Thickness |
2mm, 2.3mm, 2.5mm |
| Length |
Customized |
| Height of wave |
26mm |
| Number of wave |
6 pieces |
| Vertical overlap |
1 wave (63mm) |
| Horizontal overlap |
0.2 -0.3m |
| Componsition |
54% PVC, 44% calcium carbonate, 2% pvc stabilizer and others. |
| Quality warranty |
15 years. |
Advantage of UPVC Roofing sheet,
1.Heat insulation: The temperature difference indoor and outdoor could reach 8 to 10ºC. ASA PVC is 4 layers of PVC, this is good for heat insulation.
2.Fire proof: PVC roof sheet is a kind of safe building material, it has passed the building fire protection grade.
3.Color stable: Our roofing sheet has the anti-UV subsidiary material, it will not yellow-changing within 15 years.
4.Water proof: Water cannot pass through the pvc roof sheet.
5.Anti-corrosive: PVC roof sheet is highly resistant against chemical corrosion of acid, alkali, etc.
6.Anti-impact: PVC roof sheet has excellent load bearing performance and could withstand 150kgs. People could stand on the roof after installation.
7.Sound proof: PVC roof sheet has much less noise than other roof materials for example when it rains. lt can make noise 30db less than steel roof.
Technical Data of UPVC roof sheet, Tejas de upvc con cresta baja:
| Test item |
Test standard |
Test condition |
Test result |
|
Xenon-arc Exposure
|
ISO4892-2:2013,ISO 105-A02:1993 and
ASTM D2244-11
|
ISO4892-2:2013 cycle 4 irradiance:(0.51+-
0.02)W/(m2.nm)@340nm 102min light at (63+-3)℃
BPTT,(50+-10)10% RH 18min light and water spray
Filter:Boro/Boro Expousre period:500h
|
Grey scale (see note 1) |
(2-3) |
|
ΔE*ab (see note 2)
|
3.5 |
| Thermal resistance |
With reference to ASTM D3045-92(2010) |
150℃,30 min
|
0.0345
|
| Muriatic acid resistance |
With referenceto ISO
175-2010 and client's
requirements
|
Medium:35%(m/m) HCI(AR)
Method:Immersion method
Temperature:Room temperature
Test time :40h
|
No visible change
|
|
Hydrochloric acid resistance
|
With referenceto ISO
175-2010 and client's
requirements
|
Medium:30%(m/m) H2SQ4(AR)
Method:Immersion method
Temperature:Room temperature
Test time :48h
|
No visible change
|
|
Alkali resistance
|
With referenceto ISO
175-2010 and client's
requirements
|
Medium:30%(m/m) NaOH(AR)
Method:Immersion method
Temperature:Room temperature
Test time :48h
|
No visible change
|
| Density |
ISO 1183-1:2012
Method A
|
Absolute alcohol 23+-0.5℃ |
1.799g/cm3 |
| Flexural strength |
ISO 178:2010/amd
1:2013 Method A
|
Specimen:100*1130*2.05mm
Testing speed :1mm/min Span:50mm
|
41.3MPa |
| Flexural modulus |
4520MPa |
| Charpy unnoteched impact strength |
ISO 179-1 :2010 |
Specimen:ISO 179-1/1eU Specimen
thickness:2.05mm The capacity of the pendulum:5J
Impact speed:2.9m/s Span:62mm
|
38KJ/m2
C(complete break)
|
| Vicat softening temperature |
ISO 306:2004
Method B50
|
Specimen thickness:2.05mm
Rate of temperature:50℃/h Load:50N
|
77.3℃ |
| Tensile strength |
ISO 527-12012
and ISO 527-2:2012
|
specimen: Type 1B Specimen thickness: 2.05mm
Testing speed:5mm/min Grip separation:115mm
|
20.3MPa |
| Nominal tensile strain at break |
13% |
|
Impact resistance
|
GB/T 8814-2004 Section 5.7 and 6.7 |
Precondition:-10℃ 1h, take out and test 10s,Geo:H.25
Strick weight :1kg
Span: 200mm, Number of tested: 10
|
Numbers of
breakage:0
|
| Dimensional change |
ASTM D1204-08 |
Condition:100℃,60min,then 23℃,
50%RH,1h,Specimen:25*25cm,Madium:Talcum powar
|
X direction: -0.7% |
| Y direction: -1.3% |
| Acoustic isolation |
ISO 140-3:1995 |
Unit:DB |
13 |
| High temperature resistance |
ASTM D648-07 |
Condition:60℃,6hours |
No visible change |
| Low temperature resistance |
ASTM D648-07 |
Condition:-20℃,6hours |
No visible change |
|
Radius of
Curvature
|
JG/T 346-2011 |
Unit:m |
12 |
| Thermal Conductivity |
ASTM C518-04 |
Unit:W/(m.k)
|
0.089 |
| Fire resistance |
DIN4102-1:1998-05 |
GRADE
|
B1 |
Application of 1130 cresta UPVC roof sheet: Roofing and Wall for Factory, warehouse and farm etc.
1. how can we guarantee quality?
Always a pre-production sample before mass production;
Always final Inspection before shipment;
2.what can you buy from us?
PVC Roofing Tile, UPVC Roofing Tile, Synthetic Resin Roof Tile, APVC Roofing Tile, ASA Roofing Tile, Polycarbonate Sheet, Wall Panels
3. why choose us not from other suppliers?
we are a professional manufacturer of plastic sheet.
Our products are full, we are focusing on roofing solution and Indoor docorative material, like upvc roof sheet, ASA roof sheet and Polycarbonate roof sheet, pvc ceiling panel, deocorative roofing panel, epoxy colored sand floor.
we have 20 years experience for our researching, producing and exporting.
4. what services can we provide?
Accepted Delivery Terms: FOB,CFR,CIF,EXW,Express Delivery；
Accepted Payment Currency:USD,EUR,CNY;
Accepted Payment Type: T/T,L/C,PayPal,Western Union,Cash;
Language Spoken:English,Chinese,Spanish.
Welcome to your inquiry and visiting!!!